Abstract
After pure titanium Ingot(G2) with 400mm in diameter was manufactured, the analysis of its ingredients showed that the oxygen content was 0.073wt% and the iron content was 0.03wt%, which made ASTM Gr.2 standardization satisfactory. The processed titanium ingot produced 42mm wire rod, and hot rolling of 18th phase produced 9mm wire rod. The hardness analysis of 15.8mm wire rod, which was processed in hot rolling of 10th phase from the surface to the center, resulted in almost constant value with Hv150~200. The last 9mm wire rod had a different yield strength and elongation percentage depending on the temperature as it was led in to a hot roller. However, tensile strength revealed an approximate value and made ASTM B863 standardization satisfactory.
직경 400mm 순티타늄 잉고트(Gr2)를 제작하고 성분 분석한 결과 산소함량이 0.073wt%이고 철함량이 0.03wt%로서 ASTM Gr.2 규격을 만족하였다. 이들을 가공하여 42mm 선재를 만들고 18단 열간 압연하여 9mm 선재를 만들었다. 10단 열간 가공한 15.8mm 선재를 표면에서 부터 중심부로 가면서 경도 분석한 결과 Hv150~200로서 거의 일정한 값을 나타내고 있었다. 최종 9mm 선재는 열간 압연기에 인입시 온도에 따라 항복강도와 연신율은 달랐지만 인장강도는 근사한 값을 나타내었으며 모두 ASTM B863규격을 만족하였다.