Preparation of UV-Curable Organic-Inorganic Hybrid Hard Coating Films Using Alumina Sols and Acrylate Monomers

알루미나 졸과 아크릴레이트 단량체를 이용한 UV경화형 유-무기 하이브리드 하드코팅 막 제조

  • Hwang, Ji-Hyeon (Department of Chemical and Biochemical Engineering, Konyang University) ;
  • Song, Ki-Chang (Department of Chemical and Biochemical Engineering, Konyang University)
  • 황지현 (건양대학교 화공생명학과) ;
  • 송기창 (건양대학교 화공생명학과)
  • Published : 2011.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, UV-curing type organic - inorganic hybrid hard coating solutions were prepared from alumina sols and acrylate monomers. The mixture of alumina sols, prepared from aluminum isopropoxide, and a silane coupling agent, methacryloxypropyl trimethoxysilane(MPTMS), was used as an inorganic component. Also, the mixture of acrylate monomers, pentaerythritol triacrylate(PETA), 1,6-hexanediol diacrylate(HDDA) and dipentaerythritol hexaacrylate (DPEHA), was used as an organic component. The organic-inorganic hybrid coating solutions were obtained by mixing the inorganic component and organic component, deposited on polycarbonate substrates by spin coating and densified by UV-curing. The effect of the amount of MPTMS in the inorganic component and the irradiation time during UV-curing was studied on the properties of coating films. As a result, when 0.20 mole of MPTMS was used, the pencil hardness of coated films showed an excellent pencil hardness of 3H and also exhibited a good abrasion resistance of 2% in haze.

본 연구에서는 알루미나 졸과 아크릴레이트 단량체를 이용하여 UV 경화형 유-무기 하이브리드 하드코팅 용액을 제조하였다. Aluminum isopropoxide로부터 얻어진 알루미나 졸에 실란커플링제인 methacryloxypropyl trimethoxysilane(MPTMS)을 첨가하여 제조된 졸을 무기물 성분으로 사용하였다. 유기물 성분으로는 다양한 아크릴레이트 단량체인 pentaerythritol triacrylate(PETA), 1,6-hexanediol diacrylate(HDDA), dipentaerythritol hexaacrylate(DPEHA)를 혼합하여 사용하였다. 이후 무기물 성분과 유기물 성분을 혼합하여 유-무기 하이브리드 코팅 용액을 제조한 후, 이를 polycarbonate 기판 위에 스핀 코팅 후 UV 경화를 실시하여 도막을 형성하였다. 이때 무기물 성분 중의 MPTMS의 첨가량과 UV 경화 시간 변화가 코팅 막의 물성에 미치는 영향을 연구하였다. 그 결과 MPTMS가 0.20 mole 첨가 될 경우 코팅 막은 3H의 우수한 연필경도를 나타내었으며 haze값이 2%로 내마모성도 우수하였다.

Keywords

References

  1. Wouters, M. E. L., Wolfs, D. P., van der Linde, M. C., Hovens, J. H. P. and Tinnemans, A. H. A., "Transparent UV Curable Antistatic Hybrid Coatings on Polycarbonate Prepared by the Sol-Gel Method," Prog. Org. Coat., 51, 312-320(2004). https://doi.org/10.1016/j.porgcoat.2004.07.020
  2. Yu, Y. Y. and Chen, W. C., "Transparent Organic-Inorganic Hybrid Thin Films Prepared from Acrylic Polymer and Aqueous Monodispersed Colloidal Silica," Mater. Chem. & Phys., 82, 388-395 (2003). https://doi.org/10.1016/S0254-0584(03)00259-1
  3. Kang, D. P., Park, H. Y., Ahn, M. S. and Myung, I. H., "Properties of Sol-Gel Materials Synthesized from Colloidal Silica and Alkoxy Silanes," Polymer(Korea), 29, 242-247(2005).
  4. Oh, S. K., Chung, J. S., Lee, B. S. and Song, K. C., "Preparation of Hard Coating Solutions by Sol-Gel Reaction of Glycidoxypropyl Trimethoxysilane and Methacryloxypropyl Trimethoxysilane," Korean Chem. Eng. Res.(HWAHAK KONGHAK), 46(2), 274-278 (2008).
  5. Bae, B. S., "Inorganic-Organic Hybrid Materials Coating," Polymer Science and Technology, 12(5), 716-723(2001). https://doi.org/10.1002/pat.93
  6. Hong, J. H., UV Curing Coating, Chosun University Press, Kwang Ju(2002).
  7. Kim, D. H., Song, K. C., Chung, J. S. and Lee, B. S., "Preparation of Hard Coating Solutions using Colloidal Silica and Glycidoxypropyl Trimethoxysilane by the Sol-Gel Method," Korean Chem. Eng. Res.(HWAHAK KONGHAK), 45(5), 442-447(2007).
  8. Cheong, I. Y., Cho, K. I., Cheong S. H., Park, H. N. and Song, K. C., "Preparation of Hard Coating Solutions with High Refractive Index for Polycarbonate Sheet by the Sol-Gel Method," Korean Chem. Eng. Res.(HWAHAK KONGHAK), 45(5), 335-339(2007).
  9. Nam, D. W., Nam, B. U., Cha, B. J. and Kim, B. J., "Preparation of UV-Curable Polyurethane Modified Acrylate/$SiO_{2}$ Hybrid Film Using Sol-Gel Process," Polymer(Korea), 31, 111-116(2007).
  10. ASTM D 3359, "Standard Test Methods for Measuring Adhesion by Tape Test," ASTM International, 927-929(1997).
  11. Yoo, J. W., Kim, D. S., "UV Curing and Mechanical Properties of Urethane-Acrylate Resins," Polymer(Korea), 23(3), 376-383(1999).
  12. Rabek, J. F., Mechanisms of Photophysical Processes and Photochemical Reactions in Polymers, John Wiley & Sons, New York, NY(1987).

Cited by

  1. Effect of Addition of Pentaerythritol Triacrylate on the Properties of Waterborne Polyurethane vol.49, pp.4, 2011, https://doi.org/10.9713/kcer.2011.49.4.411
  2. Preparation of Conductive Coating Solutions by Blending Waterborne Acrylic Polyurethane Dispersion with Carbon Nanotube vol.51, pp.1, 2013, https://doi.org/10.9713/kcer.2013.51.1.73
  3. Effect of Types of Acrylic Monomers on Properties of Anti-static Waterborne Acrylic Polyurethane Dispersion vol.52, pp.4, 2014, https://doi.org/10.9713/kcer.2014.52.4.451
  4. Aniline Terminated Waterborne Polyurethane/Multi-walled Carbon Nanotube 복합 코팅 용액의 제조 및 물성 vol.50, pp.3, 2011, https://doi.org/10.9713/kcer.2012.50.3.403
  5. 아크릴 단량체의 종류 변화에 의한 수분산 폴리우레탄-아크릴 혼성 용액의 제조 vol.50, pp.3, 2011, https://doi.org/10.9713/kcer.2012.50.3.410
  6. 알카리 금속염으로부터 대전방지용 수분산 폴리우레탄 코팅용액 제조 vol.50, pp.3, 2011, https://doi.org/10.9713/kcer.2012.50.3.427
  7. Aniline Terminated Waterborne Polyurethane과 PEDOT/PSS의 블렌딩에 의한 대전방지 코팅용액의 제조 vol.50, pp.4, 2011, https://doi.org/10.9713/kcer.2012.50.4.614
  8. 마이크로 중공구를 이용한 자외선 경화 코팅 박막의 단열 특성 vol.50, pp.4, 2011, https://doi.org/10.9713/kcer.2012.50.4.621
  9. Hydroxyethyl Methacrylate와 Methyl Methacrylate의 첨가량 변화가 수분산 폴리우레탄-아크릴 혼성 용액의 물성에 미치는 영향 vol.50, pp.4, 2011, https://doi.org/10.9713/kcer.2012.50.4.632
  10. Aminopropyl Triethoxysilane과 아크릴 단량체를 이용한 Silylated Acrylic Polyurethane Dispersion의 제조 vol.50, pp.4, 2011, https://doi.org/10.9713/kcer.2012.50.4.639
  11. Alumina Sol의 제조 시 사용되는 해교제 종류가 코팅 도막의 물성에 미치는 영향 vol.54, pp.6, 2011, https://doi.org/10.9713/kcer.2016.54.6.767
  12. 콜로이드 실리카를 이용한 UV 경화형 친수성 코팅 도막 제조 vol.55, pp.6, 2011, https://doi.org/10.9713/kcer.2017.55.6.754
  13. 플라스틱 기재 위에 polysilazane을 이용한 UV 경화형 하드코팅 도막 제조 vol.56, pp.2, 2011, https://doi.org/10.9713/kcer.2018.56.2.162