Fabrication and structural observation of amorphous V-Co alloy by mechanical alloying

MA법에 의한 V-Co계 비정질합금의 제조 및 구조분석

  • Lee, Chung-Hyo (Dept. of Advanced Materials Science and Engineering, Mokpo National University)
  • 이충효 (목포대학교 신소재공학과)
  • Received : 2011.10.08
  • Accepted : 2011.11.04
  • Published : 2012.02.29
Download PDF
⟨ Previous Next ⟩

Abstract

In the present study, we investigated the effect of mechanical alloying (MA) on the formation of amorphous VCo system through solid state reaction during ball milling. Two types of powder samples, ${\sigma}$-VCo intermetallic compound and $V_{50}Co_{50}$ powder mixture, were applied as a starting materials. With increasing milling time, a structural characteristics into the amorphous state is distinctly observed from the structural factor and radial distribution by X-ray diffraction. Amorphization has been observed in all two types of samples after the milling for 120 hrs. DSC spectrum of $V_{50}Co_{50}$ powder sample milled for 60 hrs indicates a sharp exothermic peak from the crystallization at $600^{\circ}C$. The structure factor, S(Q) and radial distribution function, RDF(r), observed by X-ray diffraction gradually change into a structure characteristic of an amorphous state with increasing MA time.

본 연구에서는 출발원료로 ${\sigma}$-VCo 금속간화합물과 $V_{50}Co_{50}$ 혼합분말을 각각 사용하여 기계적 합금화에 따른 비정질화 가능성을 조사하였다. X선 회절에 의해 얻어진 전구조인자 S(Q) 및 동경분포함수 RDF(r)의 결과로부터 볼밀링이 진행됨에 따라 비정질상의 구조적 특징이 분명히 관찰되었다. 120시간 MA 처리에 의하여 두 경우 모두에서 비정질상이 생성됨을 알 수 있었다. 60시간 동안 MA 처리한 $V_{50}Co_{50}$ 분말시료의 열분석 에서는 약 $600^{\circ}C$에 비정질상의 결정화에 의한 발열 peak가 관찰되었다. X선 회절법에 의해 얻어진 전구조인자 및 동경분포함수의 분석으로부터 MA 시간에 따라 출발 결정상은 비정질상의 특징적인 원자구조로 서서히 변화함을 알 수 있었다.

Keywords

References

  1. R.B. Schwarz and W.L. Johnson, "Formation of an amorphous alloy by solid state reaction of the pure polycrystalline metals", Phys. Rev. Letters 51 (1983) 415. https://doi.org/10.1103/PhysRevLett.51.415
  2. C.C. Koch, O.B. Cavin, C.G. Mckamey and J.O. Scarbrough, "Preparation of amorphous $Ni_{60}Nb_{40}$ by mechanical alloying", Appl. Phys. Lett. 43 (1983) 1017. https://doi.org/10.1063/1.94213
  3. H. Sun, J.M.D. Coey, Y. Otani and D.P.F. Hurley, "Magnetic properties of a new series of rare-earth iron nitride: $R_{2}Fe_{17}N_{y}$", J. Phys.: Condens. Matter. 2 (1990) 64.
  4. U. Mizutani and C.H. Lee, "Effect of mechanical alloying beyond the completion of glass formation for Ni-Zr alloy powders", J. Mat. Sci. 25 (1990) 399. https://doi.org/10.1007/BF00714046
  5. J. Eckert and L. Schultz, "Glass formation and extended solubilities in mechanically alloyed cobalt-transition metal alloys", J. Less-Common Metals 166 (1990) 293. https://doi.org/10.1016/0022-5088(90)90011-8
  6. K. Aoki, A. Memezawa and T. Masumoto, "Nitrogeninduced amorphization of Ti-Zr powders during mechanical alloying", Appl. Phys. Lett. 61 (1992) 1037. https://doi.org/10.1063/1.107708
  7. P. Millet and A. Calka, "Amorphization of silicon and germanium by mechanical grinding", Mat. Sci. Eng. A181/A182 (1994) 1222.
  8. K. Sakurai, C.H. Lee, N. Kuroda, T. Fukunaga and U. Mizutani, "Nitrogen effect in mechanical alloying of immiscible Cu-V: extended X-ray absorption fine structure study", J. Appl. Phys. 75 (1994) 7752. https://doi.org/10.1063/1.356607
  9. Y. Ogino, S. Murayama and T. Yamasaki, "Influence of milling atmosphere on amorphization of chromium and Cr-Cu powders by ball milling", J. Less-Common Metals 168 (1991) 221. https://doi.org/10.1016/0022-5088(91)90304-M
  10. C.H. Lee, M. Mori, T. Fukunaga and U. Mizutani, "Structural evidence for the amorphization of mechanically alloyed Cu-Ta powders studied by neutron diffraction and EXAFS", Mat. Sci. Forum 88-90 (1992) 399. https://doi.org/10.4028/www.scientific.net/MSF.88-90.399
  11. T.B. Massalski, "Binary alloy phase diagrams", 2nd ed. ASM (1990)
  12. T. Fukunaga, N. Kuroda, C.H. Lee, T. Koyano and U. Mizutani, "Nitrogen induced amorphization observed by X-ray and neutron diffractions in the immiscible V-Cu system", J. Non-Cryst. Solids 176 (1994) 98. https://doi.org/10.1016/0022-3093(94)90217-8
  13. T. Fukunaga, "Structural change during the amorphization process by mechanical alloying", Physica B 213/214 (1995) 518. https://doi.org/10.1016/0921-4526(95)00198-I
  14. U. Mizutani and C.H. Lee, "Mechanical alloying in Cu-V and Cu-Ta systems characterized by a positive heat of mixing", Mater. Trans. JIM 36 (1995) 210. https://doi.org/10.2320/matertrans1989.36.210

Cited by

  1. VAl alloy powders by mechanical alloying vol.23, pp.1, 2013, https://doi.org/10.6111/JKCGCT.2013.23.1.051
  2. compound prepared by mechanical alloying vol.23, pp.3, 2013, https://doi.org/10.6111/JKCGCT.2013.23.3.135