Wet Etching of Stainless Steel Foil by Aqueous Ferric Chloride Solution

염화제이철 수용액에 의한 스테인레스 강판의 식각에 관한 연구

  • 이형민 (영남대학교 화학공학부) ;
  • 박무룡 ((주) LG이노텍 생산기술팀) ;
  • 박광호 ((주) LG이노텍 생산기술팀) ;
  • 박진호 (영남대학교 화학공학부)
  • Received : 2011.08.10
  • Accepted : 2011.10.05
  • Published : 2012.04.01
Download PDF
⟨ Previous Next ⟩

Abstract

Wet chemical etching of stainless steel foil by aqueous ferric chloride solution was investigated in this study. Effects of various process parameters (e.g. etchant agitation rate, etchant temperature, $Fe^{3+}$ ion concentration, free HCl concentration, specific gravity, etc.) on the etch rate was first studied, and it was found that the etch rate of AK (aluminum-killed) steel, chromium metal and stainless steel (STS430J1L alloy) follows the pseudo-first order reaction equation. When the fatigue ratio of etchant was kept under 16%, sludge was not formed in the solution, and the etched surface showed smooth roughness. The etch rate decreases as Baume of etchant increases, but the effect of free HCl concentration on the etch rate turned out to be minimal. Experimental data were compared with the calculated results from modeled equation, showing very good agreement.

염화제이철 수용액에 의한 스테인레스 강판의 식각반응에 관한 연구를 수행하였다. 식각액 교반속도, 식각온도, $Fe^{3+}$ 이온 농도, 식각액의 유리산도 및 비중 등 여러 공정변수가 식각속도에 미치는 영향에 대해 조사하였고, 그 결과, AK(aluminum-killed) 철, 크롬(chlomium) 강, 그리고 스테인레스 강(STS430J1L 합금)의 식각반응이 1차 반응식을 잘 따름을 알 수 있었다. 또한 식각액의 피로도(fatigue ratio)가 16% 이하로 유지되면 식각액 내에 슬러지가 발생하지 않으며, 식각된 강판의 표면거칠기 또한 좋아짐을 알 수 있었다. 본 연구에서 조사한 범위 내에서는, 식각액의 보메(Baume)가 증가하면 식각속도는 감소하나 유리산도가 식각속도에 미치는 영향은 미비함을 알 수 있었다. 한편 본 연구의 실험결과는 공정모델링을 통해 유도된 식각속도식의 계산결과와 잘 일치함을 알 수 있었다.

Keywords

Acknowledgement

Supported by : 한국에너지기술평가원(KETEP)

References

  1. Smith, W. F., Structure and Properties of Engineering Alloys," 2nd ed., McGraw-Hill, New York(1994).
  2. Ueda, R., "Chemical Machining by Ferric Chloride Etchant," Corrosion Eng., 38, 231-237(1989).
  3. Lewis, R. J., Sir, "Sax's Dangerous Properties of Industrial Materials," 8th ed., Van Norstrand Reinhold, New York(1992).
  4. Moscony, J. J., Maynard, R. B., Wetzel, C. M., Eshleman, C. C. and Saunders, M. H., "Optimization of the Ferric Chloride Etching of Shadow Masks," J. Sid, 4, 231(1996).
  5. Maynard, R. B., Moscony, J. J. and Saunders, M. H., "Ferric Chloride Etching of Low Carbon Steels," Rca. Rev., 45, 73(1984).
  6. Visser, A., Weissinger, D. and Ullmann, E., "Pray Etching, Mechanism of Removal, Removal Rate, and Surface Structure During Spray Etching of Stainless Steel with Ferric Chloride Part II," Galvanotechnik, 75, 14(1984).
  7. Visser, A., Weissinger, D. and Ullmann, E., "Material Processing by Spray Etching, Part II. Etching Precision," Galvanotechnik, 76, 442(1985).
  8. Allen, D. M., Hegarty, A. J. and Horne, D. F., "Surface Textures of Annealed AISI 304 Stainless Steel Etched by Aqueous Ferric Chloride-Hydrochloric Acid Solutions," Trans. Inst. Met. Finish., 59, 25(1981).
  9. Yoon, D., Lee, G. and Park, C., "Studies on the Ferric Chloride Etching of Shadow Masks," HWAHAK KONGHAK, 38(3), 393-397 (2000).
  10. Bird, R. B., Stewart, W. E. and Lightfoot, E. N., "Transport Phenomena," John Wiley & Sons, New York(1960).
  11. Ueda, R., Asakura, S., Tanozaki, Y. and Sugiura, T., Hyomen Gijutsu, 43, 48(1992). https://doi.org/10.4139/sfj.43.48
  12. Fischer, R. B. and Peters, D. G., "Quantitative Chemical Analysis," 3rd ed, W.B. Saunder Company, Philadelphia(1968).

Cited by

  1. 염화철 에칭 용액 재생을 위한 산화공정에 대한 연구 vol.26, pp.2, 2012, https://doi.org/10.7844/kirr.2017.26.2.18
  2. Spray Etching Rate Development of Stainless Steel in the Etchant for Printed Circuit Heat Exchanger Channels vol.105, pp.None, 2012, https://doi.org/10.1016/j.egypro.2017.03.957
  3. 염화철 에칭 용액 재생을 위한 액상 및 고상 산화제를 이용한 산화공정에 대한 연구 vol.23, pp.2, 2012, https://doi.org/10.7464/ksct.2017.23.2.158
  4. 철-니켈 합금 에칭구액 용매추출 공정 용액으로부터 고순도 탄산니켈 제조에 관한 연구 vol.27, pp.6, 2017, https://doi.org/10.6111/jkcgct.2017.27.6.303
  5. 파일럿 규모에서 철-니켈 합금 에칭폐액 재생 vol.23, pp.4, 2012, https://doi.org/10.7464/ksct.2017.23.4.393
  6. 에칭 폐액으로부터 용매추출과 가수분해를 이용한 니켈분말제조에 관한 연구 vol.25, pp.1, 2012, https://doi.org/10.7464/ksct.2019.25.1.014
  7. The Development of New Cost-Effective Optimization Technology for OLED Market Entry vol.17, pp.4, 2012, https://doi.org/10.15722/jds.17.4.201904.51