The Effect of Alloying Elements on Weldability and Corrosion Resistance of Austenitic Stainless Steels(I)

오스테나이트계 스테인리스강의 용접성과 내식성에 미치는 합금원소의 영향(I) - 응고균열 감수성을 중심으로 -

  • 정호신 (부경대학교 재료공학과) ;
  • 이윤용 (POSCO 스테인리스 연구그룹) ;
  • 배동수 (동의대학교 재료공학과)
  • Received : 2012.04.16
  • Accepted : 2012.06.13
  • Published : 2012.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

The interest of austenitic heat resistant stainless steels containing high Si has increased because they have higher resistance of oxidation and higher strength at high temperature than STS 310. This study carried out Varestraint test for evaluation of solidification cracking sensitivity of 14 different stainless steels. As a result of Varestraint test, all specimens solidified as primary ferrite, and solidification crack sensitivity increased with adding $N_2$ to shielding gas. Nb and W had beneficial effect on solidification crack resistance in case of less than FN 2 containing, but crack sensitivity increased with Nb and W in case of more than FN 2. Ce had beneficial effect on solidification crack resistance but impaired weld bead appearance.

Keywords

References

  1. F.Matsuda, S.Katayama and Y.Arata: Solidification Crack Susceptibility in Weld Metals of Fully Austenitic Stainless Steels(Report IX),Trans. of JWRI, 12-2 (1983), 87-92
  2. J. C. Lippold : Solidification Behavior and Cracking Susceptibility of Pulsed-Laser Welds in Austenitic Stainless Steels, Welding Journal, 73-6, 129s
  3. J. S. Lee, M. Y. Lee and K. C. Kim : Effect of Nitrogen on Weld Solidification and Solidification Cracking in Austenitic Stainless Steels, JOM-8, Helsingor, Denmark, May, 1997, 335
  4. C.J. Long and W.T. Delong: The Ferrite Content of Austenitic Stainless Steel Weld Metal, Welding Journal, 52-7(1973), 281-297s
  5. V.P.Kuyanpaa,S.A.David & C.L.White : Formation of Hot Cracks in Austenitic Stainless Steel Welds- Solidification Cracking, Welding Journal, 65-8 (1986), 203-s-212-s
  6. W. Dahl, C. Düren, H. Müsch : Einfluss Verschiedener Legierungselemente auf die Heissrissanfalligkeit eines Austenitischen Stahles beim Schweissen, Stahl u. Eisen 93, 813-822(1973)
  7. W. Dahl, C. Duren, H. Musch : Ursachen der Heissrissbildung in Schweissverbindungen eines Niobstabilisierten Stahles mit 16% Chrom und 16% Nickel. Stahl u. Eisen 93, 805-812(1973)
  8. C. H. Lee : Effect of Minor Element on Hot Cracking Susceptibility of Austenitic Stainless Steel Welds, Metals and Materials, 2-2, (1996), 81-91 https://doi.org/10.1007/BF03025950