Swelling Behaviors of Maleic Anhydride-Grafted EPDM by Treatment with Dichloroactic Acid

디클로로아세트산 처리에 따른 무수말레산-그래프트 EPDM의 팽윤 거동

  • Received : 2012.12.12
  • Accepted : 2013.01.09
  • Published : 2013.03.31
Download PDF
⟨ Previous Next ⟩

Abstract

Swelling behaviors of raw (Specimen-R) and compressed (Specimen-C) samples of maleic anhydride-grafted EPDM (MAH-g-EPDM) depending on the treatment with dichloroacetic acid were investigated. Structural characteristics of the samples were analyzed by nuclear magnetic resonance spectroscopy (NMR) and attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR). When the samples were not treated with dichloroacetic acid, the swelling ratio of Specimen-R was greater than that of Specimen-C by about twice and the swelling ratio change was negligible though the process of swelling and drying was repeated. When the samples were treated with dichloroacetic acid, the first swelling ratios were increased but the second ones were decreased. For the Specimen-C, the swelling ratio of the sample without the dichloroacetic acid treatment and the second swelling ratio of the sample treated with dichloroacetic acid were nearly the same. However, for the Specimen-R, the second swelling ratio of the sample treated with dichloroacetic acid was strikingly lower than that of the sample without the dichloroacetic acid treatment. The swelling ratio change according to the dichloroacetic acid treatment was explained by dissociation of the existing crosslinks and formation of new crosslinks.

디클로로아세트산의 처리 여부에 따른 무수말레산-그래프트 EPDM (MAH-g-EPDM) 원재료(시험편-R)와 압축 시험편(시험편-C)의 팽윤 거동을 조사하였다. 시험편의 구조적 특징은 핵자기공명분광법(NMR)과 감쇠전반사-후리에변환 적외선분광법(ATR-FTIR)으로 분석하였다. 디클로로아세트산으로 처리하지 않았을 때, 시험편-R의 팽윤비가 시험편-C의 팽윤비보다 2배 정도 컸으며 팽윤과 건조 과정을 반복하여도 팽윤비의 변화는 거의 없었다. 디클로로아세트산으로 처리하였을 때는 1차 팽윤비는 증가하였으나 건조 후 2차 팽윤비는 감소하였다. 시험편-C의 경우, 디클로로아세트산으로 처리하지 않았을 때의 팽윤비와 디클로로아세트산으로 처리한 시험편의 2차 팽윤비는 거의 유사하였다. 하지만, 시험편-R의 경우, 디클로로아세트산으로 처리한 시험편의 2차 팽윤비는 디클로로아세트산으로 처리하지 않았을 때의 팽윤비보다 크게 작았다. 디클로로아세트산으로 처리하였을 때 나타난 팽윤비 변화는 기존 가교점의 분해와 새로운 가교점의 형성으로 설명하였다.

Keywords

References

  1. S.-S. Choi and H.-S. Chung, "Influence of filler and cure systems on whitening of EPDM composites by formation of metal salt", Elast. Compos., 47, 210 (2012). https://doi.org/10.7473/EC.2012.47.3.210
  2. Y.-W Chang, J. K. Mishra, S.-K Kim, and D.-K Kim, "Effect of supramolecular hydrogen bonded network on the properties of maleated ethylene propylene diene rubber/maleated high density polyethylene blend based thermoplasticelastomer", Mater Lett., 60, 3118(2006). https://doi.org/10.1016/j.matlet.2006.02.055
  3. G. M.O. Barra, J. S. Crespo, J. R. Bertolino, V. Soldi, and A. T. Nunes Pires, "Maleic anhydride grafting on EPDM : Qualitative and quantitative determination", J. Braz. Chem. Soc., 10, 31 (1999). https://doi.org/10.1590/S0103-50531999000100006
  4. P. Pasbakhsh, H. Ismail, M.N. Ahmad Fauzi, and A. Abu Bakar, "Influence of maleic anhydride grafted ethylene propylene diene monomer (MAH-g-EPDM) on the properties of EPDM nanocomposites reinforced by halloysite nanotubes", Polym. Test., 28, 548 (2009). https://doi.org/10.1016/j.polymertesting.2009.04.004
  5. C. Shao, G. Xu, X. Shen, H. Yu, and X. Yan, "Infrared emissivity and corrosion-resistant property of maleic anhydride grafted ethylene-propylene-diene terpolymer (EPDM-g- MAH)/Cu coatings", Surf. Coat. Technol., 204, 4075 (2010). https://doi.org/10.1016/j.surfcoat.2010.05.036
  6. L. Li, B. Li, and F. Tang, "Influence of maleic anhydride- grafted EPDM and flame retardant on interfacial interaction of glass fiber reinforced PA-66", Eur. Polym. J., 43, 2604 (2007). https://doi.org/10.1016/j.eurpolymj.2007.03.008
  7. L.-P. Li, B. Yin, Y. Zhou, L. Gong, M.-B. Yang, B.-H. Xie, and C. Chen, "Characterization of PA6/EPDM-g-MA/HDPE ternary blends: The role of core-shell structure", Polymer, 53, 3043 (2012). https://doi.org/10.1016/j.polymer.2012.05.003
  8. C. Wang, J. X. Su, J. Li, H. Yang, Q. Zhang, R.N. Du, and Q. Fu, "Phase morphology and toughening mechanism of polyamide 6/EPDM-g-MA blends obtained via dynamic packing injection molding", Polymer, 47, 3197 (2006). https://doi.org/10.1016/j.polymer.2006.03.012
  9. X. Jiang, Y. Zhang, and Y. Zhang, "Study of dynamically cured PP/MAH-g-EPDM/epoxy blends", Polym. Test., 23, 259 (2004). https://doi.org/10.1016/j.polymertesting.2003.08.004
  10. Y. K. Chae, W. Y. Kang, J.-H. Jang, and S.-S. Choi, "A simple NMR method to measure crosslink density of natural rubber composite", Polym. Test., 29, 953 (2010). https://doi.org/10.1016/j.polymertesting.2010.08.003
  11. M. E. Ries, M. G. Brereton, P. G. Klein, and P. Dounis, "A proton NMR investigation of crosslinks and entanglements in polyethylene networks and star polymers", Polymer Gels and Networks, 5, 285 (1997). https://doi.org/10.1016/S0966-7822(97)00004-X
  12. J. Sohma, C. Qun, W. Yuanshen, X.-W. Qu and M. Shiotani, "Solid-state high-resolution 13C-NMR study of crosslinks in heavily gamma-irradiated polyethylen", Radial. Phys. Chem., 37, 47 (1991).
  13. S.-S Choi and S.-H Ha, "Water swelling behaviors of silica-reinforecd NBR composites in deionized water and salt solution", Ind. Eng. Chem., 16, 238 (2010). https://doi.org/10.1016/j.jiec.2010.01.052
  14. B. Guo, F. Chen, Y. Lei, X. Liu, J. Wan, and D. Jia, "Styrene-butadiene rubber/halloysite nanotubes nanocomposites modified by sorbic acid", Appl. Surf. Sci., 255, 7329 (2009). https://doi.org/10.1016/j.apsusc.2009.03.092
  15. K. Doudin, A.Ahmad, and S. A. Malaika, "Reactive processing of polymers: Structural characterisation of products by $^{1}H$ and $^{13}C$ NMR spectroscopy for glycidyl methactylate grafting onto EPR in the absence and presence of a reactive comonomer", Polym. Degrad. Stab., 94, 1599 (2009). https://doi.org/10.1016/j.polymdegradstab.2009.07.008
  16. A. O. Ramona, P. C. M. M. Magusin, V. M. Litvinov, M. V. Duin, and M. A. J. Michels, "Solid-state 1H NMR study on chemical cross-links, chain entanglements, and network heterogeneity in peroxide-cured EPDM rubbers", Macromolecules., 40, 8999 (2007). https://doi.org/10.1021/ma071015l
  17. M.-T. Sandrine, E. Fanton, N. S. Tomer, S. Rana, R.P. Singh, and J.-L. Gardette, "Photooxidation of ethylene - prophylene- diene/montmorillonite nanocomposites", Polym. Degrad. Stab., 90, 78 (2005). https://doi.org/10.1016/j.polymdegradstab.2005.01.040
  18. M. Sclavons, P. Franquinet, V. Carlier, G. Verfaillie, I. Fallais, R. Legras, M. Laurent, and F. C. Thyrion, "Quantification of the maleic anhydride grafted onto polypropylene by chemical and viscosimetric titrations, and FTIR spectroscopy", Polymer., 41, 1989 (2000). https://doi.org/10.1016/S0032-3861(99)00377-8
  19. O. P. Grigoryeva and J. Karger-Kocsis, "Melt grafting of maleic anhydride onto an ethylene-propylene-diene terpolymer (EPDM)", Eur. Polym. J., 36, 1419 (2000). https://doi.org/10.1016/S0014-3057(99)00205-0
  20. S.-W. Phang, T. Hino, M.H. Abdullah, and N. Kuramoto, "Applications of polyaniline doubly doped with p-toluene sulphonic acid and dichloroacetic acid as microwave absorbing and shielding materials", Mater. Chem. Phys., 104, 327 (2007). https://doi.org/10.1016/j.matchemphys.2007.03.031

Cited by

  1. Effects of ZnO content on microstructure and properties of maleated EPDM/zinc oxide composites vol.72, pp.5, 2015, https://doi.org/10.1007/s00289-015-1330-7