Properties of Polymer Cement Mortar Based on Styrene-Butyl Acrylate according to Emulsifier and Monomer Ratios

유화제 및 단량체비에 따른 스티렌-부틸 아크릴레이트계 폴리머 시멘트 모르타르의 특성

  • Jo, Youngkug (Department of Architectural Engineering, Chungwoon University) ;
  • Hyung, Wongil (School of Architecture, Yeungnam University)
  • Received : 2012.09.03
  • Accepted : 2013.01.02
  • Published : 2013.03.25

Abstract

The purpose of this study is to clarify the effect of the emulsifier ratio on the properties of the polymer cement mortars based on styrene-butyl acrylate (S/BA) latexes, and to obtain necessary basic data to develop appropriate latexes for cement modifiers. The polymer dispersions for cement modifiers was synthesized using styrene and butyl acrylate. Polymer cement mortars based on S/BA latexes were prepared with various monomer and emulsifier ratios, and their water-cement ratio, air content, flexural and compressive strengths, water absorption and chloride ion penetration were tested. From the test results, the maximum flexural and compressive strengths of polymer cement mortars based on S/BA latexes were obtained at a bound styrene content of 60% and an emulsifier ratio of 6%. Also, the water absorption and chloride ion penetration depth are greatly affected by the polymer-cement ratio rather than the bound styrene and emulsifier content. Accordingly, it is judged that S/BA latexes can be used place of the conventional polymer dispersions of cement modifier.

본 연구는 시멘트 혼화용 폴리머를 스티렌과 부틸 아크릴레이트를 단량체로 이용하여 유화제의 첨가량을 달리하여 합성제조하고 제조된 폴리머를 시멘트 모르타르에 혼입하여 그 특성을 파악함으로써 시멘트 혼화용으로써의 사용가능성을 확인하고자 하는 기초적 실험이다. 유화제 첨가량과 단량체비를 달리하여 스티렌-부틸 아크릴레이트(styrene/butyl acrylate)계 폴리머 시멘트 모르타르의 특성은 물-시멘트 비, 공기량, 강도, 방수성 및 염화물 이온 침투저항성을 측정하여 그 특성을 파악하고자 하였다. 연구 결과 보통 시멘트 모르타르에 비해 유화제의 첨가량이 6%일 때, S/BA의 단량체비가 60:40일 때 우수한 강도특성을 나타냈으며, 방수성과 염화물 이온 침투 저항성에서는 유화제의 첨가량과 단량체비보다는 폴리머-시멘트 비에 의해 크게 개선되는 것을 알 수 있었다. 따라서 S/BA를 시멘트 혼화용으로 혼입한 폴리머 시멘트 모르타르의 현장적용이 가능할 것으로 판단되었다.

Keywords

Acknowledgement

Supported by : 영남대학교

References

  1. W. Hyung, K. Mun, and W. Kim, J. Appl. Polym. Sci., 103, 3010 (2007). https://doi.org/10.1002/app.25459
  2. W. G. Hyung, C. Lee, and S. Park, Polymer(Korea), 34, 247 (2010).
  3. W. G. Hyung, Polymer(Korea), 33, 342 (2009).
  4. W. G. Hyung and K. J. Mun, Polymer(Korea), 32, 603 (2008).
  5. W. G. Hyung, K. J. Mun, and H. R. Song, Polymer(Korea), 32, 555 (2008).
  6. C. Satish, H. Justnes, and Y. Ohama, in "Cement Polymer Composite", in Polymer Materials Encyclopaedia, Vol 2C, pp 1389-1402 (1996).
  7. Y. Ohama, Handbook of Polymer-Modified Concrete and Mortar, Properties and Process Technology, Noyes Publications, New York, 1995.
  8. Y. W. Mai and B. Cotterell, Cement Concrete Res., 16, 646 (1986). https://doi.org/10.1016/0008-8846(86)90037-2
  9. M. Pei, Cement Concrete Res., 32, 837 (2002). https://doi.org/10.1016/S0008-8846(01)00733-5
  10. Y. W. Mai and B. Cotterell, Cement Concrete Res., 16, 646 (1986). https://doi.org/10.1016/0008-8846(86)90037-2
  11. H. Teichmann, Polymer Concrete, 5, 112 (1975).
  12. G. W. DePuy, Proceedings of the International ICPIC Workshop on Polymers in Concrete, Slovenia, pp 63-67 (1996).
  13. Y. Ohama, Report of the Building Research Institute, 65, 74 (1973).
  14. A. Shirai and Y. Ohama, Polymers in Concrete, 4, 321 (1998).
  15. Y. Jo, Y. Ohama, and K. Demura, Transactions of the Japan Concrete Institute, 15, 85 (1993).

Cited by

  1. Study on the characteristic of liner and cover material by accelerating agent type vol.27, pp.2, 2018, https://doi.org/10.5322/JESI.2018.27.2.75
  2. 재유화형 EVA 수지를 함유한 광산 폴리머-차수재의 물성 평가 vol.42, pp.4, 2018, https://doi.org/10.7317/pk.2018.42.4.637
  3. VAE 수지를 활용한 폐기물 매립지의 차수재 특성 연구 vol.28, pp.5, 2013, https://doi.org/10.5322/jesi.2019.28.5.503