The Effect of Glyceride Modified by Fatty Acid on Mechanical Properties of Silica filled Rubber Compounds

지방산으로 개질된 글리세라이드가 실리카 충진 배합고무의 가황과 기계적 물성에 미치는 영향

  • 김동욱 ((주)넥센타이어 기술연구소) ;
  • 김창환 ((주)넥센타이어 기술연구소) ;
  • 정호균 ((주)넥센타이어 기술연구소) ;
  • 강용구 ((주)넥센타이어 기술연구소)
  • Received : 2013.05.03
  • Accepted : 2013.05.21
  • Published : 2013.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

To study the effects of structural difference and fatty acid chain length of glyceride, new dispersion agents having various glyceride structures such as mono-, di-, and tri-, were prepared using glycerol extracted from palm oil and fatty acid having various chain length ranges from 12 to 18. These dispersion agents were mixed with the rubber compounds and compared with conventional metal salt dispersion agents. Glyceride dispersion agent provided remarkable improvement in silica dispersion, compared to metal salt fatty acidic one, even though the viscosity of mixtures was relatively high due to low lubricating effect, and this was approved by mechanical properties, wear properties, and Payne effect. Also, the longer in chain length of fatty acid and the smaller in numbers of fatty acid, the dispersity of silica was improved.

글리세라이드의 지방산 사슬길이 및 구조적 차이에 따른 영향을 평가하기 위하여 팜오일에서 추출된 글리세롤과 palmitic acid, stearic acid등 사슬길이가 $C_{12}{\sim}C_{18}$인 지방산을 이용하여, mono, di, tri등 다양한 글리세라이드 구조를 가진 신규 분산제를 합성하였고, 이를 실리카 충진배합물에 적용하여 기존의 금속염 분산제와 비교평가 하였다. 실험결과, 글리세라이드 분산제는 기존의 금속염 지방산 분산제 대비 혼합고무 내 윤활효과가 낮아서 혼합고무의 점도는 높으나, 실리카 분산이 크게 향상됨을 확인하였다. 이는 기계적 물성과 마모성능, Payne effect로 확인되었다. 또한 글리세라이드의 지방산 사슬길이가 길수록, 글리세롤에 중합된 지방산 수가 적을수록(tri- < di-< mono-glyceride)혼합고무 내 실리카 분산특성은 향상되었다.

Keywords

References

  1. S. Padula, Paper presented at the Tire Industry Conference, Hilton Head, SC, March 9-10, (1995).
  2. G. Kraus, "Science and Technology of Rubber", ed. by F. T. Erich, Chapter 8, Marcel Dekker, New York, 1976.
  3. W. H. waddle and L. R. Evans, Rubber Chem. Technol., 69, 377 (1996). https://doi.org/10.5254/1.3538378
  4. S. k. Kim, "아민계 분산제가 실리카 고무배합물의 물성에 미치는 영향", Polymer(Korea) Vol. 25, No. 4, pp 503-511, (2001).
  5. A. Ansarifar, International Journal of Adhension & Adhesives 25, pp 77-86, 2005. https://doi.org/10.1016/j.ijadhadh.2004.04.002
  6. Siegfried Wolff, "Chemical Aspects of Runner Reinforcement by Fillers", Rubber Chem. Technol., 69 (1996).
  7. K. A. Grosch, Rubber Chem. Technol., 69, 496 (1996).
  8. Malia Cestellano, Polymer, 46, (2005).
  9. S. C. Oh, J. H. Go, S. Lee, and N. C. Park, J. Korea Institute of Rubber Industry, 30, 115 (1995).
  10. S. S. Park, "Influence of Silica and Ingredients on Properties of Natural Rubber Compounds", Chonnam National University, 2000.
  11. Sandip Rooj, Appl. Clay Sci., 67-68, pp50-56(2012) https://doi.org/10.1016/j.clay.2012.03.005
  12. John Byer, "Zinc Oxide Reduction Becoming a Necessity" , Rubber World, 8, (2007).
  13. G. Heideman, Macromol. Symp., 657, (2006).
  14. Y. G. Kang, Elastomer, 37, 170, (2002).
  15. Struktol, "Process aids handbook"
  16. F. Clement, Rubber Chem. Technol., 74, 846, (2001).
  17. C. Gauthier, Polymer, 45, 2761, (2004). https://doi.org/10.1016/j.polymer.2003.12.081

Cited by

  1. A study of graphene oxide-reinforced rubber nanocomposite vol.131, pp.16, 2014, https://doi.org/10.1002/app.40640