Abstract
To evaluate the reliability of fly ash quality supplied to ready-mixed concrete plant using mass cylinder and hydrometer, in this research, the correlationship between the fly ash properties provided from certification and density measurement with suspension was evaluated. As a result, the reliability of the certification, except fineness and loss on ignition, all properties had a discord. Additionally, in the case of density, fineness, and L.O.I, the relation with the density measured using hydrometer showed high correlation, especially fineness was strongly related with the density measured using hydrometer. Furthermore, according to the comparative analysis with previous research, the fly ash used in this research was similar measurement with raw powder without any refining process, it is considered that the constant error of blaine test or using raw ash sample as a fly ash. In current standard regarding fly ash, the fineness range of class 2 can be changed from $3,000-4,500cm^2/g$ to $3,500-4,500cm^2/g$ for improved quality of fly ash in fineness aspect.
레미콘 공장에 납품되는 플라이애시의 품질의 신뢰성을 파악하기 위해 본 연구에서는 메스실린더와 액체비중계를 이용하여 FA 성적서에 나타난 품질특성과 혼탁액 밀도 측정값과의 상관관계를 분석하였다. 연구결과, 성적서에 나타나는 데이터의 적정성 분석으로는 분말도와 L.O.I를 제외한 모든 품질특성이 유효숫자 자릿수 또는 실험유무에 문제가 있는 것으로 분석된다. 또한, FA의 밀도, 분말도와 L.O.I의 경우는 비중계법 밀도값과 상관성이 양호한 것으로 분석되었는데, 특히 분말도의 상관성이 높은 것을 알 수 있었다. 또한 선행연구와의 비교고찰을 실시한 결과, 본 실험에 사용된 FA는 정제과정을 거치지 않은 원분과 유사한 데이터로 나타났는데, 이는 분말도 측정 방법인 Blaine 공기투과장치 간의 편차 문제 또는 양호하게 정제를 하지 않음에 기인한 것으로 사료되었다. 또한 현행 FA의 규격에도 KS L 5405 2종의 경우 분말도의 범위를 $3,000{\sim}4,500cm^2/g$에서 $3,500{\sim}4,500cm^2/g$으로 개정 한다면 레미콘 공장에 납품되는 FA 분말도 품질 향상에 크게 기여될 수 있을 것으로 사료된다.