On the effect of temperature on the threshold stress intensity factor of delayed hydride cracking in light water reactor fuel cladding

  • Received : 2017.04.12
  • Accepted : 2017.04.14
  • Published : 2017.08.25
Download PDF
⟨ Previous Next ⟩

Abstract

Delayed hydride cracking (DHC) was first observed in pressure tubes in Canadian CANDU reactors. In light water reactors, DHC was not observed until the late 1990s in high-burnup boiling water reactor (BWR) fuel cladding. In recent years, the focus on DHC has resurfaced in light of the increased interest in the cladding integrity during interim conditions. In principle, all spent fuel in the wet pools has sufficient hydrogen content for DHC to operate below $300^{\circ}C$. It is therefore of importance to establish the critical parameters for DHC to operate. This work studies the threshold stress intensity factor ($K_{IH}$) to initiate DHC as a function of temperature in Zry-4 for temperatures between $227^{\circ}C$ and $315^{\circ}C$. The experimental technique used in this study was the pin-loading testing technique. To determine the $K_{IH}$, an unloading method was used where the load was successively reduced in a stepwise manner until no cracking was observed during 24 hours. The results showed that there was moderate temperature behavior at lower temperatures. Around $300^{\circ}C$, there was a sharp increase in $K_{IH}$ indicating the upper temperature limit for DHC. The value for $K_{IH}$ at $227^{\circ}C$ was determined to be $2.6{\pm}0.3MPa$ ${\surd}$m.

Keywords

References

  1. W.L. Mudge, Effect of hydrogen on the embrittlement of zirconium and zirconium-tin alloys, Symposium on zirconium and zirconium alloys, ASM, Metals Park, OH, 1953, pp. 146-167.
  2. C.E. Coleman, D. Hardie, The hydrogen embrittlement of zirconium in slow-bend tests, J. Nucl. Mater. 19 (1966) 1-8. https://doi.org/10.1016/0022-3115(66)90123-1
  3. J.B. Bai, C. Prioul, D. Francois, Hydride embrittlement in Zircaloy-4 plate: part I, influence of microstructure on the hydride embrittlement in Zircaloy-4 at $20^{\circ}C$ and $350^{\circ}C$, Metall. Trans. 25A (1994) 1185-1197.
  4. D. Hardie, The influence of the matrix on the hydrogen embrittlement of zirconium in bend tests, J. Nucl. Mater. 42 (1972) 317-324. https://doi.org/10.1016/0022-3115(72)90082-7
  5. C.J. Simpson, C.E. Ells, Delayed hydrogen embrittlement of Zr-2.5wt% Nb, J. Nucl. Mater. 52 (1974) 289-295. https://doi.org/10.1016/0022-3115(74)90174-3
  6. D.O. Northwood, U. Kosasih, Hydrides and delayed hydrogen cracking in zirconium and its alloys, Int. Metals Rev. 28 (1983) 92-121.
  7. R. Dutton, K. Nuttall, M.P. Puls, L.A. Simpson, Mechanisms of hydrogen induced delayed cracking in hydride forming materials, Metall, Trans 8A (1977) 1553-1562.
  8. S. Sagat, M.P. Puls, SMiRT 17, Paper # G06-4.
  9. A. McMinn, E.C. Darby, J.S. Schofield, The terminal solid solubility of hydrogen in zirconium alloys, in: G.P. Sabol, G.D. Moan (Eds.), Twelfth International Symposium of Zirconium in the Nuclear Industry, 1354, ASTM STP, 2000, pp. 173-195.
  10. P. Vizaino, A.D. Banchik, J.P. Abriata, Solubility of hydrogen in Zircaloy-4: irradiation induced increase and thermal recovery, J. Nucl. Mater. 304 (2002) 96-106. https://doi.org/10.1016/S0022-3115(02)00883-8
  11. J.J. Kearns, Terminal solubility and partitioning of hydrogen in the alpha phase of zirconium, Zircaloy-2 and Zircaloy-4, J. Nucl. Mater. 22 (1967) 292-303. https://doi.org/10.1016/0022-3115(67)90047-5
  12. V. Grigoriev, Parametric study of DHC in fuel cladding, Workshop on hydrogen induced failures, November 17, 2009. Sweden.
  13. Y.S. Kim, Delayed hydride cracking of spent fuel rods in dry storage, J. Nucl. Mater. 378 (2008) 30-34. https://doi.org/10.1016/j.jnucmat.2008.04.011
  14. C.E. Coleman, The CANDU experience AECL, history: cause and remedies, Workshop on hydrogen induced failures, November 17, 2009. Sweden.
  15. F.H. Huang, W.J. Mills, Delayed hydride cracking behavior for zircaloy-2 tubing, Metall. Trans. A 22A (1991) 2049-2060.
  16. Y.S. Kim, S.C. Kwon, S.S. Kim, Crack growth pattern and threshold stress intensity factor, KIH, of Zr-2.5% Nb alloy with the notch direction, J. Nucl. Mater. 280 (2000) 304-311. https://doi.org/10.1016/S0022-3115(00)00054-4
  17. D. Yan, R.L. Eadie, The threshold behaviour of delayed hydride cracking in Zr-2.5wt%Nb, Int. J. Pressure Vessels Piping 77 (2000) 167-177. https://doi.org/10.1016/S0308-0161(99)00081-2
  18. S.-Q. Shi, M.P. Puls, Criteria for fracture initiation at hydrides in zirconium alloys, I: sharp crack tip, J. Nucl. Mater. 208 (1994) 232-242. https://doi.org/10.1016/0022-3115(94)90332-8
  19. C.E. Coleman, J.F.R. Ambler, Susceptibility of zirconium alloys to delayed hydride cracking, in: A.L. Lowe, G.W. Parry (Eds.), Zirconium in the Nuclear Industry, 633, ASTM STP, 1977, pp. 589-607.
  20. V. Grigoriev, R. Jakobsson, Delayed hydrogen cracking velocity and J-integral measurements on irradiated BWR cladding, J. ASTM Int. 2 (8) (2005) 12434. https://doi.org/10.1520/JAI12434
  21. T. Kubo, K. Sakamoto, T. Higuchi, Development of a new technique for the insitu observation of the DHC process under a SEM to measure the crack extension rate in a radial direction of Zry-2 tubes, 2008 Water Reactor Fuel Performance Meeting, October 19-23, 2008. Soul, Korea.
  22. C.F. Tiffany, J.N. Masters, Applied fracture mechanics, in: W.F. Brown Jr. (Ed.), Fracture Toughness Testing and its Applications, ASTM STP 381, American Society for Testing and Materials, Philadelphia, PA, 1965, pp. 249-277.
  23. US Nuclear Regulatory Commission, Standard review plan for spent fuel dry storage systems at a general license facility, NUREG-1536, 2009.
  24. S.-Q. Shi, M.P. Puls, Fracture strength of hydride precipitates in Zr-2.5Nb alloys, J. Nucl. Mater. 275 (1999) 312-317. https://doi.org/10.1016/S0022-3115(99)00132-4

Cited by

  1. Theoretical models of threshold stress intensity factor and critical hydride length for delayed hydride cracking considering thermal stresses vol.50, pp.7, 2017, https://doi.org/10.1016/j.net.2018.07.001
  2. Terminal solid solubility of hydrogen of optimized-Zirlo and its effects on hydride reorientation mechanisms under dry storage conditions vol.52, pp.8, 2020, https://doi.org/10.1016/j.net.2020.01.022