Abstract
The aim of this research is the feasibility analysis of the reject ash premixed cement mortar with combined aggregate. Namely, for the combined aggregate with two different qualities of aggregates, a fundamental properties of cement mortar was evaluated depending on various replacing ratios of reject ash(Ri). According to the experimental results, the combined aggregate consisted with low-quality aggregate and sea sand did not change the flow value depending on the reject ash while the combined aggregates consisted with low quality aggregate and sea sand; and consisted exploded debris sand and sea sand the increasing reject ash increased the air content with increased replacing ratio of reject ash. In the case of compressive strength, as the replacing ratio of reject ash was increased, the compressive strength was increased. It is considered that when 5% of reject ash replacing ratio made similar quality of cement mortar with favorable quality aggregate, hence, it can be suggested that 5% replacement of reject ash for desirable fluidity and compressive strength of concrete.
본 연구는 Reject Ash(Rj)를 혼합골재에 프리믹스하여 활용함에 따르는 가능성을 분석한 것이다. 즉, 서로 다른 입자특성의 저품질 잔골재인 석산 B+해사(CSb+SS), 발파석+해사(BS+SS)의 혼합골재에 대한 Rj의 치환율 변화에 따른 시멘트 모르타르의 기초적 특성을 파악하고자 하였다. 실험결과, 먼저 플로는 CSb+SS의 경우 Rj의 치환율이 증가함에 따라 거의 변화가 없었으며, 공기량은 CSb+SS와 BS+SS의 경우 모두 Rj의 치환율이 증가함에 따라 감소하는 것으로 나타났다. 압축강도는 CSb+SS와 BS+SS의 경우 모두 Rj의 치환율이 증가함에 따라 증가하는 것으로 나타났다. 따라서 혼합골재에 Rj를 5% 정도 치환할 경우에 품질이 양호한 골재를 사용한 경우와 유사한 것으로 판단되며, 5% 이상 치환할 경우에도 콘크리트의 유동성 확보 및 강도증진에 긍정적으로 기여하게 됨을 확인할 수 있었다.