Abstract
This research was performed to evaluate physical properties of polysulfide epoxy overlay material for bridge deck as part of a review for possibility of domestic application of polymer concrete for bridge deck pavement. In order to evaluate strength characteristics, compressive strength, flexural strength and bond strength were tested, and, for durability characteristics, chloride ion penetration resistance and freeze/thaw resistance were tested along with ultraviolet rays impact evaluation. The tests showed that the results met the criteria suggested by the American Concrete Institute in terms of compressive strength, flexural strength and bond strength. However, in terms of the strengths measured at various test temperatures, it was found that the epoxy material was highly dependent on temperature, and, therefore, this should be considered at the time of domestic application of the epoxy material later. Deflection characteristics was checked through flexural strength test and it was found that bridge deck pavement using the epoxy material was excellent compared to bridge deck pavement using asphalt. Furthermore, the results of chloride ion penetration resistance test and freeze/thaw resistance test were also excellent. In the evaluation of ultraviolet rays impact on epoxy slurry mixture, reduction of strain was noticed with increased strength, but the deflection characteristics after exposure to ultraviolet rays was better than the existing acryl polymer concrete. Therefore, it is concluded from the research that the polysulfide epoxy overlay material has the physical properties that are appropriate to pavement of bridge deck.
본 논문은 에폭시 계열의 폴리머 콘크리트 교면포장 공법의 국내 적용 가능성을 검토하기 위하여 교면포장용 폴리설파이드 에폭시 재료에 대한 물리 역학적 특성을 평가하기 위하여 수행하였다. 강도특성을 평가하기 위하여 압축강도, 휨강도, 접착강도 시험을 수행하였으며 내구특성 평가를 위하여 염소이온침투시험, 동결융해저항성시험, 자외선영향 평가를 실시하였다. 시험결과 압축강도, 휨강도, 접착강도 등은 미국콘크리트협회에서 제시하는 기준을 만족하는 것으로 평가되었다. 그러나 다양한 시험온도에서의 강도 시험결과에서 에폭시 재료가 온도 의존성이 큰 것으로 나타나 향후 국내 적용시 이에 대한 고려가 필요할 것으로 판단된다. 휨강도 시험을 통한 처짐에 대한 추종성은 기존 아스팔트 교면포장에 비해 우수한 것으로 평가되었다. 또한 염소이온침투 저항성, 동결융해 저항성 등에 대해서도 우수한 성질을 가진 것으로 평가되었다. 에폭시 슬러리 혼합물에 대한 자외선 영향 평가에서는 강도 증가와 파괴시 변형률 감소가 나타났으나 자외선 노출 후에도 기존 아크릴계 폴리머 콘크리트보다 처짐에 대한 추종성이 양호한 것으로 평가되었다. 따라서 폴리설파이드 에폭시 재료가 교면포장 공법으로 사용하기에 적절한 물리적 특성을 가지고 있다고 판단된다.