Rheological Properties and Foaming Behaviors of Modified PP/Nano-filler Composites

개질 폴리프로필렌/나노필러 복합체의 유변학적 특성 및 발포거동

  • Yoon, Kyung Hwa (Major in Polymer Science and Engineering, Kongju National University) ;
  • Lee, Jong Won (Major in Polymer Science and Engineering, Kongju National University) ;
  • Kim, Youn Cheol (Major in Polymer Science and Engineering, Kongju National University)
  • 윤경화 (공주대학교 고분자공학전공) ;
  • 이종원 (공주대학교 고분자공학전공) ;
  • 김연철 (공주대학교 고분자공학전공)
  • Received : 2013.02.15
  • Accepted : 2013.03.11
  • Published : 2013.07.25
Download PDF
⟨ Previous Next ⟩

Abstract

Modified polypropylene (m-PP) was fabricated by furfuryl sulphide (FS) as branching agent and m-PP/nano-filler composites were prepared with silicate and multi-walled carbon nanotube (MWCNT), using a twin screw extruder. The chemical structures and thermal properties of the m-PP were investigated by FTIR and DSC. The chemical structure of the m-PP was confirmed by the existence of =C-H stretching peak of the branching agent at 3100 $cm^{-1}$. There was no district change in melting temperature in case of m-PP, but a certain increase in crystallization temperature was notified and the increase was in the range of $10-20^{\circ}C$. The rheological properties, filler dispersion and foaming behaviors of the m-PP/nano-filler composites were investigated by dynamic rheometer, X-ray diffractometer (XRD) and scanning/transmission electron microscope (SEM/TEM). m-PP/nano-filler composites showed a high complex viscosity at a low frequency, an increase in melt elasticity, and a high shear thinning effect. Compared to pure PP, m-PP and m-PP/nano-filler composites were sufficient to enhance the foaming behavior.

이축압출기(twin screw extruder)를 이용하여 용융상태에서 furfuryl sulphide를 분지제로 개질 폴리프로필렌(modified polypropylene, m-PP)을 제조하고, 층상 실리케이트와 다중벽 탄소나노튜브(multi-walled carbon nanotube, MWCNT)와의 m-PP/나노필러 복합체를 제조하였다. m-PP의 화학구조와 열적 특성은 적외선분광기(FTIR), 시차주사열용량분석기(DSC)를 이용하여 관찰하였다. m-PP의 화학구조는 3100 $cm^{-1}$에서 나타나는 분지제의 =C-H 신축진동피크를 이용하여 확인하였고, 용융온도는 큰 변화를 보이지 않았지만 결정화온도는 $10-20^{\circ}C$ 가량 증가하였다. m-PP/나노필러 복합체의 유변학적 특성과 분산성 및 발포거동은 동적유변측정기, X-선 회절분석기(XRD), 주사/투과전자현미경(SEM/TEM)을 이용하여 관찰하였다. m-PP/나노필러 복합체의 낮은 주파수 영역에서의 복합점도와 용융탄성이 증가하였으며, 전단담화(shear thinning) 효과 또한 증가하였다. 순수 PP와 비교할 때 m-PP와 m-PP/나노필러 복합체의 발포 거동 개선효과가 우수한 것을 확인하였다.

Keywords

Acknowledgement

Supported by : 한국연구재단

References

  1. S. J. Kim, C. S. Yoo, and C. S. Ha, Journal of Adhesion and Interface, 10, 23 (2009).
  2. H. W. Chung, J. S. Lee, W. N. Kim, and J. C. Hyun, Korean J. Rheology, 8, 119 (1996).
  3. S. Li, M. Xiao, D. Wei, H. Xiao, F. Hu, and A. Zheng, Polymer, 50, 6121 (2009). https://doi.org/10.1016/j.polymer.2009.10.006
  4. J. Li, C. Zhou, and W. Gang, Polym. Test., 22, 217 (2003). https://doi.org/10.1016/S0142-9418(02)00085-5
  5. O. M. Istrate and B. Chen, Soft Matter, 7, 1840 (2011). https://doi.org/10.1039/c0sm01052a
  6. Y. J. Yim, M. K. Seo, H.Y. Kim, and S. J. Park, Polymer(Korea), 36, 494 (2012).
  7. S. U. Lee, I. H. Oh, J. H. Lee, K. Y. Choi, and S. G. Lee, Polymer(Korea), 29, 271 (2005).
  8. J. H. Ko, J. C. Kim, and J. H. Chang, Polymer(Korea), 33, 333 (2009).
  9. K. H. Yoon, D. Y. Shin, and Y. C. Kim, Polymer(Korea), 36, 245 (2012).
  10. E. Borsig, M. van Duin, A. D. Gotsis, and F. Picchioni, Eur. Polym. J., 44, 200 (2008). https://doi.org/10.1016/j.eurpolymj.2007.10.008
  11. C. J. Tsenoglou and A. D. Gotsis, Macromolecules, 34, 4685, (2001). https://doi.org/10.1021/ma010370n
  12. B. Y. Lee, P. Dahal, H. S. Kim, S. Y. Yoo, and Y. C. Kim, Appl. Chem. Eng., 23, 388 (2012).
  13. D. Hong, K. J. Yoon, and K. Y. Lee, Polymer(Korea), 26, 61 (2002).
  14. F. Yu, H. Zhang, R. Liao, H. Zheng, W. Yu, and C. Zhou, Eur. Polym. J., 45, 2110 (2009). https://doi.org/10.1016/j.eurpolymj.2009.03.011
  15. S. P. Lonkar and R. P. Singh, Thermochim. Acta, 49, 63 (2009).
  16. S. J. Choi, K. H. Yoon, H. S. Kim, S. Y. Yoo, and Y. C. Kim, Polymer(Korea), 35, 356 (2011).
  17. M. Yamaguchi and M. H. Wagner, Polymer, 47, 3629 (2006). https://doi.org/10.1016/j.polymer.2006.03.052
  18. H. J. Kim, J. J. Lee, J. C. Kim, and Y. C. Kim, J. Indus. Eng. Chem., 16, 406 (2010). https://doi.org/10.1016/j.jiec.2009.08.006

Cited by

  1. Effect of Thermal History on the Physical Properties of Nylon66 vol.25, pp.1, 2014, https://doi.org/10.14478/ace.2013.1116
  2. 호모 폴리프로필렌을 이용한 고강도 폴리프로필렌 폼의 제조를 위한 공정 최적화 연구 vol.42, pp.3, 2013, https://doi.org/10.7317/pk.2018.42.3.364